V. Patel | USGS Science

USGS2001

Chemical and engineering properties of fired bricks containing 50 weight percent of class F fly ash

The generation of fly ash during coal combustion represents a considerable solid waste disposal problem in the state of Illinois and nationwide. In fact, the majority of the three million tons of fly ash produced from burning Illinois bituminous coals is disposed of in landfills. The purpose of this study was to obtain a preliminary assessment of the technical feasibility of mitigating this solid waste problem by making fired bricks with the large volume of fly ash generated from burning Illinois coals. Test bricks were produced by the extrusion method with increasing amounts (20-50% by weight) of fly ash as a replacement for conventional raw materials. The chemical characteristics and engineering properties of the test bricks produced with and without 50 wt% of fly ash substitutions were analyzed and compared. The properties of the test bricks containing fly ash were at least comparable to, if not better than, those of standard test bricks made without fly ash and met the commercial specifications for fired bricks. The positive results of this study suggest that further study on test bricks with fly ash substitutions of greater than 50wt% is warranted. Successful results could have an important impact in reducing the waste disposal problem related to class F fly ash while providing the brick industry with a new low cost raw material.

Energy Sources↗

USGS1999

Utilization of the gypsum from a wet limestone flue gas desulfurization process

The authors have been developing a process which converts FGD-gypsum to ammonium sulfate fertilizer with precipitated calcium carbonate as a by-product during the conversion. Preliminary cost estimates suggest that the process is economically feasible when ammonium sulfate crystals are produced in a granular size (1.2 to 3.3 mm), instead of a powder form. However, if additional revenue from the sale of the PCC for higher-value commercial application is applicable, this could further improve the economics of the process. Ammonium sulfate is known to be an excellent source of nitrogen and sulfur in fertilizer for corn and wheat production. It was not known what impurities might co-exist in ammonium sulfate derived from scrubber gypsum. Before the product could be recommended for use on farm land, the impurities and their impact on soil productivity had to be assessed. The objectives of this phase of the study were to evaluate the chemical properties of ammonium sulfate made from the FGD-gypsum, to estimate its effects on soil productivity, and to survey the marketability of the two products. The results of this phase of the study indicated that the impurities in the ammonium sulfate produced would not impose any practical limitations on its use at application levels used by farmers. The market survey showed that the sale price of solid ammonium sulfate fertilizer increased significantly from 1974 at $110/ton to 1998 at $187/ton. Utilities currently pay $16 to $20/ton for the calcium carbonate they use in their flue gas scrubber system. The industries making animal-feed grade calcium supplement pay $30/ton to $67/m-ton for their source of calcium carbonate. Paper, paint, and plastic industries pay as much as $200 to $300/ton for their calcium carbonate filers. The increased sale price of solid ammonium sulfate fertilizer and the possible additional revenue from the sale of the PCC by-product could further improve the economics of producing ammonium sulfate from FGD-gypsum.

Conference Paper↗